NS-502 lead-free high-temperature wave soldering and reflow soldering tray tooling materials

Stone lead-free is a composite material made of glass fiber (cloth), high-temperature resistant resin, and nano reinforced materials. It is a new type of composite material developed based on the upgrade of synthetic stone. Compared to synthetic stones, it has higher properties such as high temperature resistance, anti-static, chemical corrosion resistance, no pilling, and high flatness.

Widely used in fields such as electronics, aviation, and shipbuilding. In the field of protective materials for electronic manufacturing welding, this material is a suitable choice for machining parts that are easy to process, require high strength, and maintain bending of thin plates during hot and heating processes.

Suitable for PCB and electronics industries such as insulation testing fixtures, wave soldering, reflow soldering, SMT surface mounting, furnace trays, and tin furnace fixtures.

NS-502 lead-free high-temperature wave soldering and reflow soldering tray tooling materials

Fill out this field
Please enter a valid email address.
Fill out this field

Description

Characteristics & Applications For template test PCB & ICT applications.
Colour Black
Standard Sheet Size (mm) 1020*1220 1220*2440
Thickness (mm) 3.0 ~ 30
Specific Gravity (g/cm 3) 1.95-2.05
Water Absorption E-24/50+D-24/23 ≤0.20 %
specific heat J/(Kg.k)
Insulation Resistance C-90/20/65 10⁴~10¹¹Ω
Flexural Strength ⊥Mpa 23±2℃ 400
150±2℃ 100
185±2℃
10-6/Kcoefficieni of linear thermal expansion 204 00C 12
Continuous working temperature ℃ 280
Short-term working temperature ℃ 10-20S 305
thickness tolerance mm 0.10
planeness tolerance (3O5*3O5)mm 0.10

Application

NS-502 Lead-free high temperature wave soldering, reflow welding tray tooling material

Related Applications:

No results found.

Download

Description

Datasheet

Contact us

Fill out this field
Please enter a valid email address.
Fill out this field